Film base: Difference between revisions
Jump to navigation
Jump to search
→Acetate base
| Line 7: | Line 7: | ||
===Acetate base=== | ===Acetate base=== | ||
"Used in the early 1930s mostly for small gauges, then was widely used post 1950s to replace nitrate base. Often refered to as "safety film". Acetate" base in modern exhibition settings usually refers to '''triacetate''' base. '''Diacetate''' was used on some early safety film, but you won't see it very often under normal circumstances (whatever THOSE are!). Older acetate prints tend to be more brittle and prone to warping as they lose moisture. Acetate is thicker and tends to break when stressed | "Used in the early 1930s mostly for small gauges, then was widely used post 1950s to replace nitrate base. Often refered to as "safety film". Acetate" base in modern exhibition settings usually refers to '''triacetate''' base. '''Diacetate''' was used on some early safety film, but you won't see it very often under normal circumstances (whatever THOSE are!). Older acetate prints tend to be more brittle and prone to warping as they lose moisture. Acetate is thicker and tends to break when stressed. Use only tape or cement splices. | ||
* Acetate base prints can suffer from vinegar syndrome if not stored at the proper temperature and humidity levels. Make sure they are kept cool and dry, and separate out any prints you suspect of having vinegar syndrome (even the beginning stages) as it can spread from one print to another. | |||
===Nitrate=== | ===Nitrate=== | ||